Explosion at a Methanation Reactor
The day before the incident, the outlet pipe connected to methanation reactor started leaking gas, which contains hydrogen. The leak was temporarily eliminated by a pressurised plug. On the day of the incident, the pipe leaked again, and the same plugging method was still used to stop the leak. This occurred without shutting down the unit and taking safety measures. Approximately one hour later, a sudden explosion occurred at the inlet line of the methanation reactor. The welded joint of outlet pipes that connected to the methanation furnace was operating for a long time in the high temperature hydrogen containing medium. Under this condition, hydrogen embrittlement took place, producing local defects and eventually opening up. The released hydrogen ignited and exploded.
Event Date
April 23, 2011
Record Quality Indicator
Region / Country
Event Initiating System
Classification of the Physical Effects
Nature of the Consequences
Cause Comments
The immediate cause was hydrogen corrosion which caused a crack and a gas release. Attempts to stop the leak by temporary measures were executed without stopping the operations and no additional safety measures being put in place were definitively part of the root causes. According to the source (See reference), the company did not implemented the safety operation procedures prescribed by the "Pressure Pipeline Management Regulations", and specifically the "Special Equipment Safety Technical Specifications" (TSG D0001-2009 Pressure Pipeline Safety Technical Supervision Regulations-Industrial Pipelines) and "General Specifications for Standardization of Hazardous Chemical Business Units" (AQ3013-2008).
Facility Information
Application Type
Application
Specific Application Supply Chain Stage
Components Involved
outlet pipe
Storage/Process Medium
Location Type
Location description
Industrial Area
Operational Condition
Pre-event Summary
The outlet pipe from the methanation reactor was leaking and had been temporary repaired by a pressurized plug.
Lessons Learned
Lessons Learned
According to the source (See reference), in the petrochemical industry, the corrosion problems caused by the poor processing raw materials are increasing, as well as leakage in production, storage and transportation. On top of that, the operating periods of materials and systems are getting longer. To ensure uninterrupted long-term operation of the process systems, the use of pressure plugging technology is also increasing. However, plugging under pressure is characterised by a poor working environment (generally high temperature, high pressure, flammable and explosive, toxic and harmful, and coexistence of various harsh conditions): therefore accidents are very likely to occur during the operation. How to ensure safe conditions? It is important to investigate how to quickly and effectively stop leaks under pressure, and standardize the plugging technology under pressure to form national standards or industry standards.Suggested measures Increase investment in safety, strengthen detection, and investigate and control potential safety hazards. Strengthen safety education and training for employees to improve safety awareness. Further implement the unit's safety production rules and regulations, special equipment inspection and maintenance plan and safety production target responsibility system, and strictly implement special equipment operating procedures. Strengthen supervision, form a working mechanism combining safety production supervision and industry supervision and guidance, strengthen cooperation, and further strengthen safety education, guidance, supervision and inspection of enterprises. Carry out research on the safety application of hot air plugging technology and standardize it.
Event Nature
Emergency Action
unknown
Detonation
No
Deflagration
No
High Pressure Explosion
No
High Voltage Explosion
No
Source Category
References
References
Report and analysis at renrendoc
https://www.renrendoc.com/paper/126162606.html
(accessed May 2023)