As part of preparing for material disposal, a small fire occurred within a fume hood as a researcher was combining several spent ammonia borane (AB) samples that had previously been stored uncovered in the back of the hood for 6+ months. These AB samples consisted primarily of two 40-gram products of a 50wt% AB in silicone oil that had been thermally dehydrogenated. A small amount of unreacted AB slurry is believed to also have been present.

During project clean-up, partially spent (thermally reacted) ammonia borane (AB) residue from a previous experiment was mixed with a small amount of water to rinse the residue from its container. The water reacted with the spent AB resulting initially in a large heat release followed immediately by a fire. It appears that the water addition view more

An incident occurred when Ti-doped sodium alanate was exposed to air, apparently resulting in an unstable compound that experienced a rapid exothermic reaction.

The sample consisted of mechanically milled NaAlH4 with 4% TiCl3 dopant which was prepared in an argon atmosphere. The sample was sealed and placed in the probe head of an NMR magic angle-spinning (MAS) rotor and spun at approximately 9,000-13,000 rpm. During the process, the sealing cap dislodged and exposed the sample to ambient air for a little less than 24 hours. When discovered, the sample was visually inspected and showed no evidence of oxidation. The sample was re-capped and returned to an argon environment for removal. Most of the sample material was removed using a small stainless steel needle, but a residual view more